ASTM B579 - 73(2015) - Standard Specification for Electrodeposited Coatings of Tin-Lead Alloy (Solder Plate)

Related Standards

ASTM B579 - 73(2015)

Standard Specification for Electrodeposited Coatings of Tin-Lead Alloy (Solder Plate)

Status : Current   Published : January 2015

Format
PDF

Format
HARDCOPY



1.1 This specification covers the requirements for electrodeposited tin-lead coatings on fabricated articles of iron, steel, copper, and copper alloys, to protect them against corrosion ( Note 1), to improve and preserve solderability over long periods of storage, and to improve anti-galling characteristics.

Note 1:  Some corrosion of tin-lead coatings may be expected in outdoor exposure. In normal indoor exposure, tin-lead is protective on iron, copper, and copper alloys. Corrosion may be expected at discontinuities (pits or pores) in the coating. Porosity decreases as the thickness is increased. A primary use of the tin-lead coating (solder) is with the printed circuit industry as a solderable coating and as an etch mask material.

1.2 This specification applies to electrodeposited coatings containing a minimum of 50 % and a maximum of 70 % tin. The specification applies to mat, bright, and flow-brightened tin-lead coatings.

Note 2:  Tin-lead plating baths are composed of tin and lead fluoborates and of addition agents to promote stability. The final appearance may be influenced by the addition of proprietary brighteners. Without brighteners, the coatings are mat; with brighteners, they are semibright or bright. Flow-brightened coatings are obtained by heating mat coatings to above the melting point of tin-lead for a few seconds and then quenching; palm oil, hydrogenated oils, or fats are used as a heat-transfer medium at a temperature of 260 ± 10°C (500 ± 20°F), but other methods of heating are also in use. The maximum thickness for flow-brightening is about 7.5 μm (0.3 mil); thicker coatings tend to reflow unevenly. The shape of the part is also a factor; flat surfaces tend to reflow more unevenly than wires or rounded shapes ( Note 3).

Note 3:  Volatile impurities in tin-lead coatings will cause bubbling and foaming during flow-brightening resulting in voids and roughness. The impurities can arise from plating solution addition agents and from improper rinsing and processing.

1.3 This specification does not apply to sheet, strip, or wire in the unfabricated form or to threaded articles having basic major diameters up to and including 19 mm (0.75 in.).




Standard NumberASTM B579 - 73(2015)
TitleStandard Specification for Electrodeposited Coatings of Tin-Lead Alloy (Solder Plate)
StatusCurrent
Publication Date03 January 2015
Normative References(Required to achieve compliance to this standard)No other standards are normatively referenced
Informative References(Provided for Information)No other standards are informatively referenced
Descriptors Electrodeposited coatings, tin-lead alloy (solder, plate) Solder, tin-lead alloy Tin-lead
ICS25.220.40
PublisherASTM
FormatA4
DeliveryYes
Pages5
File Size91 KB
Price£40.00


 Your basket
Your basket is empty

Multi-user access to over 3,500 medical device standards, regulations, expert commentaries and other documents


Tracked Changes

Understand the changes made to a standard with our new Tracked Changes version


BSOL

The faster, easier way to work with standards


Worldwide Standards
We can source any standard from anywhere in the world